PA11 - HP Nylon
Characteristics
Technology: MJF (Multi Jet Fusion)
Build Time: 72h (Big size parts or bulk / high volume orders will be longer)
Color: Black; Natural Gray
Tolerance: ±0.3mm (Within 100mm) or ±0.4% (Above 100mm)
Recommended Wall Thickness: > 1.0mm
Max Build Size: 370x276x360mm
Min Build Size: 5mm x 5mm x 5mm / 10mm x 2mm x 2mm
Advantages: Excellent heat resistance, high toughness, and superior chemical and impact resistance. Heat deflection temperature: 185 ℃
Features: Surface exhibits a grainy texture with visible particulate patterns.
Applications: Ideal for industrial structural components, snap-fit assemblies, sporting goods, and electronic device housings, and other functional components.
Material Properties
| Measurement | Test Method | Value |
| Tensile strength，max load, XY | ASTM D638 | 52 MPa/7542 psi |
| Tensile strength, max load, Z | ASTM D638 | 52 MPa/7542 psi |
| Tensile modulus, XY | ASTM D638 | 1800 MPa/261 ksi |
| Tensile modulus, Z | ASTM D638 | 1800 MPa/261 ksi |
| Elongation at break, XYZ | ASTM D638 | 50% |
| Flexural strength, XY | ASTM D790 | 70 MPa/10150 psi |
| Flexural strength, Z | ASTM D790 | 70 MPa/10150 psi |
| Flexural modulus, XY | ASTM D790 | 1650 MPa/240 ksi |
| Flexural modulus, Z | ASTM D790 | 1700 MPa/246 ksi |
| Izod impact notched (@ 3.2 mm, 23°C), XY | ASTM D256 Test Method A | 6 kJ/m2 |
| Izod impact notched (@ 3.2 mm, 23°C), Z | ASTM D256 Test Method A | 5 kJ/m2 |
| Heat deflection temperature (@ 0.45 MPa, 66 psi), XYZ | ASTM D648 Test Method A | 185°C/365°F |
| Heat deflection temperature (@ 1.82 MPa, 264 psi), XYZ | ASTM D648 Test Method A | 54°C/129°F |